The ENiCrMo-4 alloy contains nickel, molybdenum and chromium, with tungsten added. For welding materials of similar composition, can be used for dissimilar welding between nickel-based alloys and stainless steel, as well as surfacing and surfacing. Due to its high molybdenum content, the alloy exhibits high resistance to stress cracking, pitting and crevices. The ENiCrMo-4 electrode for metal covering and cladding was created for the excellent ability of a piece of equipment to remain in all positions, especially for misplacement welding, being malleable, easy to form and weld, and excellent resistance to stress corrosion cracking in chloride-containing solutions with high chromium and molybdenum content.
- Used for welding materials of similar composition. This low carbon, nickel-chromium-molybdenum filler metal can also be used for dissimilar welding between nickel base alloys and stainless steels, as well as for surfacing and cladding.
- Due to high molybdenum content, this alloy offers excellent resistance to stress corrosion cracking and pitting and crevice corrosion
|Condition||Tensile strength Mpa (Ksi)||Yield strength Mpa (Ksi)||Elongation %|
|AWS Reaulrement||690（100）min||Not specified||25 min|
|Typical Results as weled||730（106）||540（78）||39|
|Process||Diameter in(mm)||Voltage (V)||Flat||Vertical and Overhead|
|SMAW||3/32 (2.4mm)||24 – 28||70 – 85||65 – 75|
|SMAW||1/8 (3.2mm)||26 – 30||85 – 110||80 – 90|
|SMAW||5/32 (4.0mm)||28 – 32||110 – 140||100 – 120|
|SMAW||3/16 (4.8mm)||28 – 32||120 – 160||110 – 130|
|Diameter in(mm)||Length in(mm)||Packaging|
|3/32 (2.4)||12 (229)||10lbs (4.54kgs)|
|1/8 (3.2)||14 (356)||10lbs (4.54kgs)|
|5/32 (4.0)||14 (356)||10lbs (4.54kgs)|
|3/16 (4.8)||14 (356)||10lbs (4.54kgs)|